Tekijä: | Alam, Sardar Bilal |
Työn nimi: | Single Compartment Micro Direct Glucose Fuel Cell |
Julkaisutyyppi: | Diplomityö |
Julkaisuvuosi: | 2009 |
Sivut: | 131 Kieli: eng |
Koulu/Laitos/Osasto: | Elektroniikan, tietoliikenteen ja automaation tiedekunta |
Oppiaine: | Optiikka ja molekyylimateriaalit (S-129) |
Valvoja: | Franssila, Sami |
Ohjaaja: | |
Elektroninen julkaisu: | http://urn.fi/URN:NBN:fi:aalto-201203091374 |
OEVS: | Sähköinen arkistokappale on luettavissa Aalto Thesis Databasen kautta.
Ohje Digitaalisten opinnäytteiden lukeminen Aalto-yliopiston Harald Herlin -oppimiskeskuksen suljetussa verkossaOppimiskeskuksen suljetussa verkossa voi lukea sellaisia digitaalisia ja digitoituja opinnäytteitä, joille ei ole saatu julkaisulupaa avoimessa verkossa. Oppimiskeskuksen yhteystiedot ja aukioloajat: https://learningcentre.aalto.fi/fi/harald-herlin-oppimiskeskus/ Opinnäytteitä voi lukea Oppimiskeskuksen asiakaskoneilla, joita löytyy kaikista kerroksista.
Kirjautuminen asiakaskoneille
Opinnäytteen avaaminen
Opinnäytteen lukeminen
Opinnäytteen tulostus
|
Sijainti: | P1 Ark S80 | Arkisto |
Avainsanat: | micro fuel cells direct glucose fuel cell microfabrication |
Tiivistelmä (eng): | Micro fuel cells have received considerable attention over the past decade due to their high efficiency, large energy density, rapid refuelling capability and their inherent non-polluting aspect. An air breathing abiotically catalyzed single compartment micro direct glucose fuel cell (SC-µDGFC) has been developed using microfabrication technologies. The single compartment of the fuel cell was shared by the anode and cathode that had an interdigitating comb electrodes configuration. The SC-µDGFC compartment was formed of polydimethylsiloxane (PDMS) which exhibits high permeability to oxygen and served as the membrane through which oxygen from ambient environment was able to permeate to the cathode. To minimize the losses associated with fuel crossover, two features were incorporated in the fuel cell: (i) silver was used as the catalyst to selectively reduce oxygen in the presence of glucose and (ii) cathodes were made 25-45µm higher than the anode to reduce access of oxygen to the anode with nickel or platinum catalyst. For 1M glucose/2M KOH solution, an initial OCV of 120-160mV was recorded, which gradually decreased with time and stabilized at 60-75mV. For a fuel cell tested without PDMS membrane, maximum OCV of 135mV and power density of 0.38µW/cm2 was obtained. |