Author:Andersson, Markus Tomas
Title:The evaluation of carbide structures and sensitization phenomena of the EN 1.4016 steel during line annealing process
Teräksen EN 1.4016 karbidirakenteiden ja herkistymisen arviointi linjahehkutus prosessin aikana
Publication type:Master's thesis
Publication year:2009
Pages:73 + [42]      Language:   eng
Department/School:Materiaalitekniikan laitos
Main subject:Materiaalitiede   (MT-45)
Supervisor:Hannula, Simo-Pekka
Instructor:Penttinen, Ilkka ; Palosaari, Mikko
OEVS:
Electronic archive copy is available via Aalto Thesis Database.
Instructions

Reading digital theses in the closed network of the Aalto University Harald Herlin Learning Centre

In the closed network of Learning Centre you can read digital and digitized theses not available in the open network.

The Learning Centre contact details and opening hours: https://learningcentre.aalto.fi/en/harald-herlin-learning-centre/

You can read theses on the Learning Centre customer computers, which are available on all floors.

Logging on to the customer computers

  • Aalto University staff members log on to the customer computer using the Aalto username and password.
  • Other customers log on using a shared username and password.

Opening a thesis

  • On the desktop of the customer computers, you will find an icon titled:

    Aalto Thesis Database

  • Click on the icon to search for and open the thesis you are looking for from Aaltodoc database. You can find the thesis file by clicking the link on the OEV or OEVS field.

Reading the thesis

  • You can either print the thesis or read it on the customer computer screen.
  • You cannot save the thesis file on a flash drive or email it.
  • You cannot copy text or images from the file.
  • You cannot edit the file.

Printing the thesis

  • You can print the thesis for your personal study or research use.
  • Aalto University students and staff members may print black-and-white prints on the PrintingPoint devices when using the computer with personal Aalto username and password. Color printing is possible using the printer u90203-psc3, which is located near the customer service. Color printing is subject to a charge to Aalto University students and staff members.
  • Other customers can use the printer u90203-psc3. All printing is subject to a charge to non-University members.
Location:P1 Ark TKK  108   | Archive
Keywords:sensitization
ferritic stainless steel
chrominum carbíde
line-annealing
DL-EPR test
herkistyminen
ferriittinen ruostumaton teräs
kromikarbidi
linja hehkutus
DL-EPR
Abstract (eng): In this thesis the carbide structures and sensitization of the ferritic stainless steel EN 1.4016 with chromium content of 17 wt-% were studied.
The carbide structures and sensitization resulting from the batch annealing-and the line annealing process and two different hot rolling procedures used in the line annealing production line (the Full-Tandem-and the Steckel-Tandem procedures) were investigated.
Also the effect of the occasionally occurring process delays was studied for different durations at 800 °C, 850 °C and 900 °C.

SEM-and TEM-imaging showed that the carbides were mostly spherical or nodular by shape and they situated, as expected, mainly on the grain boundaries, depending on the annealing temperature (the resulting undercooling), however, this had no correlation to the measured degree of sensitization.
The DL-EPR tests showed, that the degree of sensitization did not vary much between the batch annealed (the reference) and the best line annealed products.
The comparison between the hot rolling procedures did not either yield any clear difference.

The DL-EPR results proved that only one of the line annealing routes was successful in decreasing the occurred sensitization by recrystallization.
In all other cases, the line annealing process increased, even doubled, the degree of sensitization.
This was mostly, however, removed during the final stages of the manufacturing process.
Abstract (fin): Tässä opinnäytetyössä tutkittiin ferriittisessä ruostumattomassa teräksessä EN 1.4016 syntyviä karbidirakenteita ja esiintyvää herkistymistä valmistusprosessin seurauksena.
EN 1.4016 sisältää kromia noin 17 p-% verran.
Eri tuotanto prosessien (kupu-uuni hehkutus reitin ja linja hehkutus reittien) samoin kuin kahden eri kuumavalssaus prosessin (Full-Tandem- ja Steckel-Tandem prosessien) seurauksena syntynyttä herkistymistä ja muodostuneita karbidirakenteita tutkittiin DLEPR testillä ja tietyiltä osin SEM:llä ja TEM:llä.
Myös ajoittain tapahtuvien prosessi seisahdusten vaikutusta tutkittiin, prosessointi lämpötilojen ollessa 800 °C, 850 °C ja 900 °C.

SEM- ja TEM-kuvaukset paljastivat, että karbidit olivat enimmäkseen pyöreähköjä tai nodulaarisia muodoiltaan ja sijoittuivat odotetusti enimmäkseen raerajoille.
Niiden sijainti riippui hehkutuslämpötilasta (alijäähtymisen määrästä sammutuksen yhteydessä).
Havaittujen karbidien sijainnilla ei kuitenkaan näyttänyt olevan yhteyttä mitattuun herkistymisasteeseen.
DL-EPR testit osoittivat, että herkistymisaste ei juuri eronnut kupu-uuni hehkutetun referenssinäytteen ja suotuisimpien linja hehkutettujen näytteiden välillä.
Myöskään kuumavalssausprosessien vertailu ei tuottanut selkeää tulosta siitä, kumpi prosessi on parempi herkistymisen kannalta.

DL-EPR tulokset osoittivat, että vain yksi linjahehkutusreiteistä alensi herkistymisastetta rekristallisaation seurauksena.
Kaikissa muissa tapauksissa linja hehkutus vain lisäsi, jopa kaksinkertaisti herkistymisasteen arvon.
Tämä vahinko kuitenkin korjaantui yhtä tapausta lukuun ottamatta valmistusprosessin loppuvaiheissa.