Author:Kellokoski, Kristiina
Title:Thermal yellowing of bleached chemical pulps
Valkaistujen sellujen lämpökellertyminen
Publication type:Master's thesis
Publication year:2013
Pages:82 s. + liitt. 9      Language:   eng
Department/School:Kemian tekniikan korkeakoulu
Main subject:Puutuotetekniikka   (P3001)
Supervisor:Vuorinen, Tapani
Instructor:Vänskä, Emilia
Electronic version URL: http://urn.fi/URN:NBN:fi:aalto-201402121370
OEVS:
Electronic archive copy is available via Aalto Thesis Database.
Instructions
close

Reading digital theses in the closed network of the Aalto University Harald Herlin Learning Centre

In the closed network of Learning Centre you can read digital and digitized theses not available in the open network.

The Learning Centre contact details and opening hours: https://learningcentre.aalto.fi/en/harald-herlin-learning-centre/

You can read theses on the Learning Centre customer computers, which are available on all floors.

Logging on to the customer computers

  • Aalto University staff members log on to the customer computer using the Aalto username and password.
  • Other customers log on using a shared username and password.

Opening a thesis

  • On the desktop of the customer computers, you will find an icon titled:

    Aalto Thesis Database

  • Click on the icon to search for and open the thesis you are looking for from Aaltodoc database. You can find the thesis file by clicking the link on the OEV or OEVS field.

Reading the thesis

  • You can either print the thesis or read it on the customer computer screen.
  • You cannot save the thesis file on a flash drive or email it.
  • You cannot copy text or images from the file.
  • You cannot edit the file.

Printing the thesis

  • You can print the thesis for your personal study or research use.
  • Aalto University students and staff members may print black-and-white prints on the PrintingPoint devices when using the computer with personal Aalto username and password. Color printing is possible using the printer u90203-psc3, which is located near the customer service. Color printing is subject to a charge to Aalto University students and staff members.
  • Other customers can use the printer u90203-psc3. All printing is subject to a charge to non-University members.
Location:P1 Ark Aalto  1680   | Archive
Keywords:additives
antioxidants
impregnation
pulp
thermal yellowing
UVRR
antioksidantit
impregnointi
lisäaineet
lämpökellertyminen
sellu
Abstract (eng):When bleached chemical pulps are dried or processed with plastics, high temperatures are often needed.
Elevating temperatures cause thermal degradation, e.g. yellowing of pulps.
As ISO brightness is an important quality parameter of commercial pulp grades, stability of pulp against colour changes during heat exposure is a significant subject that needs research.
Inhibition of thermal yellowing has drawn researchers interest to the topic, but uniform and effective solutions still does not exist.
The preliminary experiments in this thesis are divided in to two parts: determine appropriate heating equipment with relevant heat treatment parameters, and develop and evaluate an impregnation method.
Performance of the impregnation method was evaluated by a sheet weight gain, scanning electron microscopy, and confocal Raman microscopy measurements after impregnations.One of the objectives in primary experiments was to investigate and compare thermal yellowing of filter paper, sticker base paper and eleven commercial pulps.
Heat treatments were primarily executed with a planar laminator at temperature 190°C and pressure 10 kg/cm2 during 10 minutes.
Differences between the samples were analysed with ISO brightness and ultraviolet resonance Raman spectroscopy measurements before and after thermal treatments.
The main objective of the primary experiments was to study the effects of different antioxidants and additives on thermal yellowing of filter paper and fully bleached chemical pulps.
In addition, impact of two different pH ranges was studied by using buffer solutions with pH 5 and 8.
The laboratory sheets of filter paper and ECF bleached softwood kraft pulp were impregnated in ethyl acetate and 1-propanol solutions with the dissolved mixture of the additives (Hydrotalcite, stearic acid) or antioxidants (BHT, antioxidant 168 and Hostanox).
The similar approach was applied with the buffer solutions.
In addition to the impregnation experiments, effects of three different plastic laminates (polypropylene, polypropylene-maleic anhydride and high-density polyethylene) on thermal yellowing of ECF bleached chemical pulp were studied.The most drastic thermal yellowing tendency was detected with the pulp and paper sheets impregnated with buffer solution of pH 5.
The results imply that thermal degradation reactions are significantly accelerated in acidic conditions.
The impregnation with additives and antioxidants showed only a slight inhibition on thermal yellowing.
In addition, pure ethyl acetate solution accelerated thermal yellowing distinctively.
The plastic coatings had noticeable effects on thermal yellowing of sheets and differences in the wetting behaviour between plastic grades were detected.
Polypropylene-maleic anhydride is typically used as a compatibilizer and thus it showed excellent wetting properties.
Polypropylene and especially high-density polyethylene did not absorb thoroughly into the sheet samples.
Abstract (fin):Kun valkaistuja sellumassoja kuivataan tai prosessoidaan muovien kanssa, tarvitaan korkeita lämpötiloja.
Lämpötilan noustessa tapahtuu selluloosan lämpöhajoamista, mikä aiheuttaa esimerkiksi kuitujen kellertymistä.

Valkaistujen kaupallisten massojen ISO-vaaleus on yksi tärkeimmistä laatuparametreista ja siten myös massojen stabilointi värimuutoksia vastaan lämpökäsittelyn aikana vaatii tutkimusta.
Tämän diplomityön esikokeet jaettiin kahteen osaan, joista ensimmäinen käsitteli sopivan lämpökäsittelylaitteiston valintaa ja käsittelyparametrien optimointia.

Toinen osa esikokeita käsittää impregnointimenetelmän kehityksen ja sen toimivuuden arvioinnin.
Menetelmän toimivuutta tutkittiin impregnoitujen laboratorioarkkien painon lisäyksen perusteella, pyyhkäisyelektronimikroskopialla (SEM) sekä samapolttopisteisellä ramanmikroskopialla (CRM).
Diplomityön ensisijaisten kokeiden tavoitteena oli tutkia suodatinpaperin, tarrantaustapaperin ja 11 kaupallisen, valkaistun sellun lämpökellertymistä.
Lämpökäsittelyt suoritettiin Weverk-tasolaminaattorilla 190°C lämpötilassa ja 10 kg/cm2 paineessa 10 minuutin ajan.
Arkit analysoitiin ISO-vaaleusmittausten ja UV-resonanssiramanspektroskopian avulla ennen ja jälkeen lämpökäsittelyn.Kokeellisen osan tavoitteena oli myös tutkia eri antioksidanttien ja lisäaineiden vaikutusta valkaistujen sellujen lämpökellertymiseen.
Lisäksi pH:n vaikutusta tutkittiin käyttämällä pH 5 ja 8 puskuriliuoksia.
Antioksidanttien (BHT, antioksidantti 168 ja Hostanox) ja lisäaineiden (hydrotalkiitti, steariinihappo) vaikutusta tutkittiin impregnoimalla suodatinpaperia sekä ECF-valkaistuja havuselluarkkeja etyyliasetaatti- ja 1-propanoli liuoksissa, joihin antioksidantit ja lisäaineet liuotettiin.
Impregnointimenetelmää käytettiin myös puskuriliuosten tapauksessa.
Impregnointikäsittelyjen lisäksi tässä diplomityössä tutkittiin kolmen eri muovilaminaatin (polypropyleeni, polypropyleeni-maleiinianhydridi ja korkeatiheyksinen polyeteeni) vaikutusta suodatinpaperin ja ECF-valkaistun havusellun lämpökellertymiseen.
Voimakkain lämpökellertyminen havaittiin pH 5 puskuriliuoksessa impregnoiduissa arkeissa.

Tulokset indikoivat, että happamat olosuhteet kiihdyttävät merkittävästi lämpökellertymisreaktioita.
Antioksidanttien ja lisäaineiden havaittiin johtavan vähäisiin lämpökellertymistä inhiboiviin reaktioihin.
Puhtaan etyyliasetaattiliuoksen huomattiin myös kiihdyttävän lämpökellertymistä.

Muovilaminaateilla oli huomattavia vaikutuksia arkkien lämpökellertymiseen.
Muovilaminaattien välillä oli huomattavia eroja myös arkkien kostutuksessa.
Kytkentäaineena käytettävä polypropyleeni-maleiinianhydridi osoitti erinomaista kykyä kostuttaa arkki läpikotaisin, kun taas vahvasti hydrofobiset polypropyleeni ja korkeatiheyksinen polyeteeni eivät imeytyneet arkkiin läpikotaisin.