Author:Lindqvist, Sebastian
Title:Fracture mechanical characterization of multimetal welds
Multimetal hitsien murtumismekaaninen karakterisointi
Publication type:Master's thesis
Publication year:2014
Pages:105      Language:   eng
Department/School:Materiaalitekniikan laitos
Main subject:Koneenrakennuksen materiaalitekniikka   (MT3001)
Supervisor:Hänninen, Hannu
Instructor:Karjalainen-Roikonen, Päivi
Electronic version URL: http://urn.fi/URN:NBN:fi:aalto-201406252220
OEVS:
Electronic archive copy is available via Aalto Thesis Database.
Instructions

Reading digital theses in the closed network of the Aalto University Harald Herlin Learning Centre

In the closed network of Learning Centre you can read digital and digitized theses not available in the open network.

The Learning Centre contact details and opening hours: https://learningcentre.aalto.fi/en/harald-herlin-learning-centre/

You can read theses on the Learning Centre customer computers, which are available on all floors.

Logging on to the customer computers

  • Aalto University staff members log on to the customer computer using the Aalto username and password.
  • Other customers log on using a shared username and password.

Opening a thesis

  • On the desktop of the customer computers, you will find an icon titled:

    Aalto Thesis Database

  • Click on the icon to search for and open the thesis you are looking for from Aaltodoc database. You can find the thesis file by clicking the link on the OEV or OEVS field.

Reading the thesis

  • You can either print the thesis or read it on the customer computer screen.
  • You cannot save the thesis file on a flash drive or email it.
  • You cannot copy text or images from the file.
  • You cannot edit the file.

Printing the thesis

  • You can print the thesis for your personal study or research use.
  • Aalto University students and staff members may print black-and-white prints on the PrintingPoint devices when using the computer with personal Aalto username and password. Color printing is possible using the printer u90203-psc3, which is located near the customer service. Color printing is subject to a charge to Aalto University students and staff members.
  • Other customers can use the printer u90203-psc3. All printing is subject to a charge to non-University members.
Location:P1 Ark Aalto  2153   | Archive
Keywords:DMW
strength mismatch
digital image correlation
true stress-true strain
eriparihitsi
lujuuden epäsopu
J-R käyrä
todellinen jännitys ja venymä
Abstract (eng):Dissimilar metal weld (DMW) is a type of weld that connects different metals.
In nuclear power plants DMWs connect a low alloy steel (LAS) to a stainless steel (SS) through a weld metal.
The DMWs in nuclear power plants are prone to flaws.
The severity of a flaw in a DMW can be estimated by integrity assessment methods.
However, current assessment methods are not accurate enough.
One way to develop better assessment methods is to accurately characterize crack growth behaviour and material parameters in DMWs.

In this thesis two types of DMW mock-ups, common in nuclear power plants, were examined to characterize material properties and crack growth behaviour in DMWs.
The other mock-up was a narrow gap DMW (MU1), and the other mock-up contained a weld with a buttering layer (MU3).
The hardness and strength across the weld was measured for both mock-ups.
Also true stress-true strain curves at different locations in the weld were measured by digital image correlation (DIC).
Additionally, the fracture toughness close to the LAS/weld fusion line in MU1 was measured according to the procedure in ASTM E1820.
The fracture toughness was measured with single edge bend (SEB) specimens with the starter notch at the LAS/weld fusion line, 0,5 mm towards the LAS, or 0,5 mm towards the weld metal.
The crack deviation in the SEB specimens was quantitatively evaluated from optical and profilometer images.

Strength mismatch between the harder LAS and softer weld metal is 110 MPa for MU1, and 80 MPa for MU3.
A strength peak for both mock-ups was measured close to the LAS/weld fusion line.
For the MU1 the peak strength was in the LAS, and for the MU3 at the LAS/weld fusion line.
The fracture toughness of MU1 is largest for the SEB specimens with the crack in the weld metal, and smallest for the specimens with the crack at the LAS/weld fusion line.
The cracks of the specimens with the starter notch in the LAS deviate towards the softer weld, and these cracks can grow through microstructures with higher strength than at the crack tip origin.
The cracks initiating at the other locations do not deviate into adjacent zones.
Abstract (fin):Ydinvoimaloissa eriparihitsi koostuu matalaseosteisesta teräksestä (LAS), joka on yhdistetty ruostumattomaan teräkseen (SS) hitsausliitoksella.
Tämän tyyppisiin eriparihitseihin ydintyy ydinvoimaloissa säröjä.
Säröjen kriittisyyden arvioimiseen tarvitaan tarkempia arviointimenetelmiä nykyisten epätarkkojen menetelmien tilalle.
Yksi tapa kehittää näitä arviointimenetelmiä on tuottaa tarkempaa tietoa säröjen käyttäytymisestä ja materiaaliparametreista eriparihitseissä.

Tässä työssä säröjen käyttäytymistä ja materiaaliominaisuuksia tutkittiin kahden erityyppisen ydinvoimalaitoksen eriparihitsissä, joista valmistettiin kokeita varten mallikappaleet.
Toinen mallikappaleista koostui kapearailohitsistä (MU1), ja toinen koostui puskurointikerroksesta (MU3).
Molemmista mallikappaleista mitattiin kovuus ja lujuus hitsin yli.
Myös todellinen jännitys-todellinen venymä mitattiin digitaalisella kuvakorrelaatio (DIC) tekniikalla.
Lisäksi MU1:tä mitattiin murtumissitkeys ASTM E1820 mukaan.
Murtumissitkeys mitattiin SEB sauvoilla, joiden esilovi oli joko LAS/hitsi sularajalla, 0,5 mm sularajasta LAS:a kohden, tai 0,5 mm sularajasta hitsiä kohden.
Särön poikkeamaa alkuperäiseltä särönkasvutasolta tutkittiin SEB sauvoista kvalitatiivisesti optisilla ja profilometri-mittauksilla.

Lujuuden epäsopu kovemman LAS:n ja pehmeämmän hitsimetallin välillä on 110 MPa MU1:lle, ja 80 MPa MU3:lle.
Lujuuspiikki mitattiin molemmille eriparihitseille LAS/hitsi sularajan läheisyydestä.
MU1:n piikki oli LAS:ssa ja MU3:n LAS/hitsi sularajalla.
Murtumissitkeys on suurin SEB näytteillä, joiden esiväsytyssärö on hitsimetallissa, ja pienin sularajalla.
Säröt, joiden alkulovi on LAS:ssa poikkeavat kohti pehmeämpää hitsiainetta, mutta samalla nämä säröt kasvavat mikrorakenteen läpi, jossa on suurempi lujuus kuin särön ydintymispaikassa.
Muualta ydintyvät säröt eivät kasva kohti viereisiä vyöhykkeitä.
ED:2014-08-03